Estimation of growth rate in unidirectionally solidified multicrystalline silicon by the growth-induced striation method

Multicrystalline silicon was grown by unidirectional solidification method using the accelerated crucible rotation technique. The application of the accelerated crucible rotation technique in unidirectional solidification method induced growth striations across the axial direction of the grown crystal. This striation pattern was observed from carbon concentration distribution, obtained by using Fourier transform infrared spectroscopy. The generated striation pattern was found to be weak and discontinuous. Some striations were absent, probably due to back melting, caused during each crucible rotation. From the growth striations and applied time period in crucible rotation, the growth rate was estimated by using Fourier transformation analysis.     

Use of a range scaling method to determine alanine/water stopping power ratios

A phantom composed of alanine dosimeter material has been constructed and depth–dose measurements made in a 10 MeV electron beam. The results have demonstrated the feasibility of using relative depth–dose measurements to determine stopping power ratios in materials of dosimetric interest. Experimental stopping power ratios for alanine dosimeter material and water agreed with the data of ICRU Report 37 within the uncertainty of the experiment (±1.2% at a 95% confidence level).     

Eu- and Yb-induced reconstructions on a vicinal Si(1 0 0) surface

Early stages of rare-earth metal (Yb and Eu) growth on a vicinal, single-domain Si(1 0 0)2 × 1 surface have been studied in the coverage range of 0.1-0.3 monolayer (ML) by low energy electron diffraction, scanning tunneling microscopy, and synchrotron radiation photoemission spectroscopy. We show that Yb induces the 2 × 3 periodicity in the whole range of coverage studied. The 2 × 3 reconstruction coexists with the local 3 × 2/4 × 2 structure at about 0.2 ML of Yb. In contrast, Eu forms the 3 × 2 periodicity at 0.1-0.2 ML, whereas this structure is converted into the 2 × 3 phase at about 0.3 ML. The atomic arrangement and electronic properties of these reconstructions and the adsorbate-mediated modification of surface morphology are investigated.     

Stationary entanglement between macroscopic mechanical oscillators

We show that the optomechanical coupling between an optical cavity mode and two movable cavity mirrors is able to entangle two different macroscopic oscillation modes of the mirrors. This continuous variable entanglement is maintained by the light bouncing between the mirrors and is robust against thermal noise. In fact, it could be experimentally demonstrated using present technology. Received 2 September 2002 / Received in final form 10 October 2002 Published online 7 January 2003     

Synthesis and conformational investigation of tetrapeptide analogues of the fragment B23-B26 of insulin

Tetrapeptides containing one of a set of four different α,α-dialkyl glycines at the C-terminus were synthesized by conventional methods in solution and their conformational behavior investigated by ¹H NMR spectroscopy in connection with molecular mechanics calculations. The results were consistent with conformations stabilized by a γ-turn in the case of compounds with alkyl groups larger than methyl, while the corresponding Aib derivative did not exhibit intramolecular hydrogen bonding.     

The glow curve structure for the LiF:Mg,Cu,Na,Si TL detector with dopants concentrations and sintering temperatures

The glow curve structures for LiF:Mg,Cu,Na,Si TL detectors with various dopant concentrations and sintering temperatures were investigated for the improvement of the glow curve structure and sensitivity of the TL detector. The dopant concentrations were varied over the following ranges: Mg (0–0.25 mol%), Cu (0–0.07 mol%), Na and Si (0–1.5 mol%). With increasing Cu concentration, the intensity of the main peak was intensified and reached a maximum at a concentration of 0.05 mol%. The high-temperature peak was reduced. The dependency of the main peak intensity on the Mg concentration exhibits a sharp maximum at 0.2 mol%. The intensity of the high-temperature peak tends to rise slightly with increasing Mg concentration. It was found that the optimum concentrations of the dopants in the LiF:Mg,Cu,Na,Si TL material are Mg: 0.2 mol%, Cu: 0.05 mol%, Na and Si: 0.9 mol%. The dependency of the main peak intensity on sintering temperature exhibits a very sharp maximum at 830°C. The high-temperature peak was rapidly reduced after 825°C.     

Synthesis and association of poly(N,N‐dimethylacrylamide) copolymers with perfluorocarbon pendent groups connected through polyethylene‐glycol tethers

The synthesis is reported of copolymers of N,N‐dimethylacrylamide (DMA) and methacrylates containing 2,2′‐dihydroperfluorodecanoyl (RF) groups separated from the methacrylate by long polyethylene glycol (PEG) tether groups (between 1000 and 14,000 Da). At concentrations of between 1 and 8 wt % the copolymers with macromonomer contents of 1 mol % or less give gels in organic solvents such as dioxane, THF, or methanol, as well as in water. Given the low molecular weights, this indicates very efficient association of very low numbers of RF groups. Association and gel formation is enormously enhanced in the presence of longer PEG tethers. This is consistent with smaller poly(N,N,‐dimethylacrylamide) (PDMA) intermolecular excluded volume effects that are mediated by the longer PEG tethers and possibly by the incompatibility of PEG and PDMA that may lead to the formation of PEG microdomains. This increases the local concentrations of the RF groups in the PEO domains that are not diluted by the PDMA chains, as would be the case in the absence of PEG tethers. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 360–373, 2004     

Polymerization of 1,3‐dienes with functional groups. III. Free‐radical polymerization of N,N‐diethyl‐2‐methylene‐3‐butenamide

Free‐radical homo‐ and copolymerization behavior of N,N‐diethyl‐2‐methylene‐3‐butenamide (DEA) was investigated. When the monomer was heated in bulk at 60 °C for 25 h without initiator, rubbery, solid gel was formed by the thermal polymerization. No such reaction was observed when the polymerization was carried out in 2 mol/L of benzene solution with with 1 mol % of azobisisobutyronitrile (AIBN) as an initiator. The polymerization rate (R_p) equation was R_p ∝ [DEA]^1.1[AIBN]^0.51, and the overall activation energy of polymerization was calculated 84.1 kJ/mol. The microstructure of the resulting polymer was exclusively a 1,4‐structure where both 1,4‐E and 1,4‐Z structures were included. From the product analysis of the telomerization with tert‐butylmercaptan as a telogen, the modes of monomer addition were estimated to be both 1,4‐ and 4,1‐addition. The copolymerizations of this monomer with styrene and/or chloroprene as comonomers were also carried out in benzene solution at 60 °C. In the copolymerization with styrene, the monomer reactivity ratios obtained were r₁ = 5.83 and r₂ = 0.05, and the Q and e values were Q = 8.4 and e = 0.33, respectively. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 999–1007, 2004     

Comparative behavior of polybutadiene and polynorbornene‐based latices prepared by dispersion ring‐opening metathesis polymerization with a poly(ethylene oxide) macromonomer

This study critically examines the similarities and differences between poly(ethylene oxide) (PEO) stabilized latices of polynorbornene and polybutadiene. Features such as the kinetics of copolymerization of norbornene and cyclooctadiene with a macromonomer of PEO, the particles' size and morphology, the type of copolymer formed, and the stability of these latices were investigated and the results obtained are considered. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2705–2716, 2004